| J606 | According with GB E6016-D1 Corresponding with AWS E9016-D1 | |||||||||||||||||||||
| Introduction: J606 is a kind of low-alloy high strength steel electrode with low-hydrogen potassium type coating. AC/DC. All-position welding. When welding with AC, its performance stability is a little worse than that when welding with DC. | ||||||||||||||||||||||
| Uses: Used for welding medium-carbon steel and low-alloy high strength steel structures with corresponding strength, such as 15MnVN, etc. | ||||||||||||||||||||||
Chemical Composition of Deposited Metal (%)
| ||||||||||||||||||||||
Mechanical Properties of Deposited Metal
| ||||||||||||||||||||||
| Diffusible Hydrogen Content in Deposited Metal:≤4.0ml/100g(Glycerine Hydrogen Test) | ||||||||||||||||||||||
| X-ray Radiographic Inspection:ⅠDegree | ||||||||||||||||||||||
Reference Current(AC, DC+)
| ||||||||||||||||||||||
| Instructions: 1.The electrodes must be baked under about 350℃ for an hour before welding, and used as soon as baking is completed. 2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared. 3.When welding, short arc must be used and stringer bead is suitable. 4.If the weldments are very thick, they should be preheated under over 150℃ and cooled slowly after welding. | ||||||||||||||||||||||
| J606 | According with GB E6016-D1 Corresponding with AWS E9016-D1 | |||||||||||||||||||||
| Introduction: J606 is a kind of low-alloy high strength steel electrode with low-hydrogen potassium type coating. AC/DC. All-position welding. When welding with AC, its performance stability is a little worse than that when welding with DC. | ||||||||||||||||||||||
| Uses: Used for welding medium-carbon steel and low-alloy high strength steel structures with corresponding strength, such as 15MnVN, etc. | ||||||||||||||||||||||
Chemical Composition of Deposited Metal (%)
| ||||||||||||||||||||||
Mechanical Properties of Deposited Metal
| ||||||||||||||||||||||
| Diffusible Hydrogen Content in Deposited Metal:≤4.0ml/100g(Glycerine Hydrogen Test) | ||||||||||||||||||||||
| X-ray Radiographic Inspection:ⅠDegree | ||||||||||||||||||||||
Reference Current(AC, DC+)
| ||||||||||||||||||||||
| Instructions: 1.The electrodes must be baked under about 350℃ for an hour before welding, and used as soon as baking is completed. 2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared. 3.When welding, short arc must be used and stringer bead is suitable. 4.If the weldments are very thick, they should be preheated under over 150℃ and cooled slowly after welding. | ||||||||||||||||||||||