| D112 | According with GB EDPCrMo-A1-03 | ||||||||||
| Introduction: D112 is a kind of CrMo surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||||
| Uses: Used for welding the surfaces of worn-out low-carbon, medium-carbon and low-alloy parts, especially suitable for surfacing welding and repairing of mining machinery and agricultural machinery. | |||||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||||
| Hardness of Surfacing Layer:HB≥220 | |||||||||||
| Reference Current(AC, DC)
| |||||||||||
| Instructions: 1.The electrodes must be baked under about 150℃ for an hour before welding. 2.Large work pieces should be preheated to about 200℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||||
| D112 | According with GB EDPCrMo-A1-03 | ||||||||||
| Introduction: D112 is a kind of CrMo surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||||
| Uses: Used for welding the surfaces of worn-out low-carbon, medium-carbon and low-alloy parts, especially suitable for surfacing welding and repairing of mining machinery and agricultural machinery. | |||||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||||
| Hardness of Surfacing Layer:HB≥220 | |||||||||||
| Reference Current(AC, DC)
| |||||||||||
| Instructions: 1.The electrodes must be baked under about 150℃ for an hour before welding. 2.Large work pieces should be preheated to about 200℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||||