| D212 | According with GB EDPCrMo-A4-03 | ||||||||
| Introduction: D212 is a kind of CrMo surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||
| Uses: Used for single layer or multi-layer surfacing welding on the surfaces of all kinds of worn-out parts, such as gears, buckets, mining machinery, etc. | |||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||
| Hardness of Surfacing Layer:HRC≥50 | |||||||||
| Reference Current(AC, DC)
| |||||||||
| Instructions: 1.The electrodes must be baked under about 150℃ for an hour before welding. 2.Large work pieces should be appropriately preheated to about 300℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||
| D212 | According with GB EDPCrMo-A4-03 | ||||||||
| Introduction: D212 is a kind of CrMo surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||
| Uses: Used for single layer or multi-layer surfacing welding on the surfaces of all kinds of worn-out parts, such as gears, buckets, mining machinery, etc. | |||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||
| Hardness of Surfacing Layer:HRC≥50 | |||||||||
| Reference Current(AC, DC)
| |||||||||
| Instructions: 1.The electrodes must be baked under about 150℃ for an hour before welding. 2.Large work pieces should be appropriately preheated to about 300℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||