| D132 | According with GB EDPCrMo-A2-03 | ||||||||||
| Introduction: D132 is a kind of CrMo surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||||
| Uses: Used for welding the surfaces of worn-out low-carbon, medium-carbon and low-alloy parts, especially suitable for surfacing welding and repairing of the surface of worn-out parts of mining machinery and agricultural machinery. | |||||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||||
| Hardness of Surfacing Layer:HRC≥30 | |||||||||||
| Reference Current(AC, DC)
| |||||||||||
| Instructions: 1.The electrodes must be baked under about 150℃ for an hour before welding. 2.Large work pieces should be appropriately preheated to about 300℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||||
| D132 | According with GB EDPCrMo-A2-03 | ||||||||||
| Introduction: D132 is a kind of CrMo surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||||
| Uses: Used for welding the surfaces of worn-out low-carbon, medium-carbon and low-alloy parts, especially suitable for surfacing welding and repairing of the surface of worn-out parts of mining machinery and agricultural machinery. | |||||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||||
| Hardness of Surfacing Layer:HRC≥30 | |||||||||||
| Reference Current(AC, DC)
| |||||||||||
| Instructions: 1.The electrodes must be baked under about 150℃ for an hour before welding. 2.Large work pieces should be appropriately preheated to about 300℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||||