| D102 | According with GB EDPMn2-03 | ||||||||
| Introduction: D102 is a kind of ordinary manganese surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||
| Uses: Used for surfacing welding or repairing of the surfaces of worn-out low-carbon, medium-carbon and low-alloy steel parts, such as axles, gears, blades of mixers, etc. | |||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||
| Hardness of Surfacing Layer:HB≥220 | |||||||||
| Reference Current(AC, DC)
| |||||||||
| Instructions: 1.The electrodes must be baked under about 250℃ for an hour before welding. 2.Large work pieces should be preheated to about 200℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||
| D102 | According with GB EDPMn2-03 | ||||||||
| Introduction: D102 is a kind of ordinary manganese surfacing electrode with lime-titania type coating. AC/DC. It has stable arc and good slag detachability. | |||||||||
| Uses: Used for surfacing welding or repairing of the surfaces of worn-out low-carbon, medium-carbon and low-alloy steel parts, such as axles, gears, blades of mixers, etc. | |||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||
| Hardness of Surfacing Layer:HB≥220 | |||||||||
| Reference Current(AC, DC)
| |||||||||
| Instructions: 1.The electrodes must be baked under about 250℃ for an hour before welding. 2.Large work pieces should be preheated to about 200℃ before surfacing welding, and the rust and the oil stains on the surfaces of the welded parts should be cleared away. | |||||||||