| A002 | According with GB E308L-16 Corresponding with AWS E308L-16 | ||||||||||||||||||||
| Introduction: A002 is a kind of ultra-low-carbon Cr19Ni10 stainless steel electrode with lime-titania type coating. The carbon content of the deposited metal is lower than or equal to 0.04%. It has excellent intercrystalline corrosion-resistance and welding performance. The coating has red-resistance, high strength and good blowhole-resistance. AC/DC. | |||||||||||||||||||||
| Uses: Used for welding ultra-low-carbon Cr19Ni10 stainless steel structures, and also used for 0Cr19Ni11Ti corrosion-resistant stainless steel structures whose working temperature is lower than 300℃. Mainly used for the production of equipment of synthetic fiber, chemical fertilizers, petroleum, etc. | |||||||||||||||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||||||||||||||
| Mechanical Properties of Deposited Metal
| |||||||||||||||||||||
| Reference Current(AC, DC+)
| |||||||||||||||||||||
| Instructions: 1.The electrodes should be baked under 200-250℃ for an hour before welding. 2.Direct current had better be used and the current should not be too strong. | |||||||||||||||||||||
| A002 | According with GB E308L-16 Corresponding with AWS E308L-16 | ||||||||||||||||||||
| Introduction: A002 is a kind of ultra-low-carbon Cr19Ni10 stainless steel electrode with lime-titania type coating. The carbon content of the deposited metal is lower than or equal to 0.04%. It has excellent intercrystalline corrosion-resistance and welding performance. The coating has red-resistance, high strength and good blowhole-resistance. AC/DC. | |||||||||||||||||||||
| Uses: Used for welding ultra-low-carbon Cr19Ni10 stainless steel structures, and also used for 0Cr19Ni11Ti corrosion-resistant stainless steel structures whose working temperature is lower than 300℃. Mainly used for the production of equipment of synthetic fiber, chemical fertilizers, petroleum, etc. | |||||||||||||||||||||
| Chemical Composition of Deposited Metal (%)
| |||||||||||||||||||||
| Mechanical Properties of Deposited Metal
| |||||||||||||||||||||
| Reference Current(AC, DC+)
| |||||||||||||||||||||
| Instructions: 1.The electrodes should be baked under 200-250℃ for an hour before welding. 2.Direct current had better be used and the current should not be too strong. | |||||||||||||||||||||